Uobičajeni materijali za vijke u mojoj zemlji uključuju čelik 45, 40Cr, nitrirani čelik, 38CrMoAl i legure za-visoke temperature.
1) Čelik 45 je jeftin i ima dobru obradivost, ali slabu otpornost na habanje i koroziju. Toplinska obrada: kaljenje i temperiranje HB220-270, visokofrekventno kaljenje HRC45-48.
2) 40Cr has better performance than 45 steel, but it often needs to be plated with a layer of chromium to improve its corrosion and wear resistance. However, the chromium plating layer has high requirements; too thin a layer is prone to wear, while too thick a layer is prone to peeling, which accelerates corrosion. Therefore, it is less commonly used. Heat treatment: quench and temper HB220-270, hard chromium plating HRC>55.
3) Nitrirani čelik i 38CrMoAl imaju izvrsne ukupne performanse i naširoko se koriste. Debljina sloja nitriranja je općenito 0,4-0,6 mm. Međutim, ovaj materijal ima nisku otpornost na koroziju klorovodikom i relativno je skup.
4) Visoko{1}}temperaturni legirani materijali bolji su od drugih materijala. Ovaj materijal ne zahtijeva oplatu i uglavnom se koristi za proizvodnju vijaka bez halogena-u strojevima za injekcijsko prešanje. Ovaj materijal ima visoku otpornost na oksidaciju i koroziju i može se toplinski obraditi do 55-60 stupnjeva Celzijusa.